MGO Filler Dry may be used as joint filler, finish and fixative for the reinforcement mat to prevent damage due to structural settlement or thermal expansion. The filler has good waterproofing properties and high mechanical strength, shock and abrasion resistance. Thanks to its high binding properties, MGO Filler Dry is highly elastic and characterised by low water solubility. The product adapts to any type of environment, from coastal areas exposed the continuous corrosive action of salt; to mountain areas subject to continuous temperature fluctuations and highly polluted industrial areas.
Between +5°C and +40°C; Relative Humidity <80%.
PREPARATION OF THE MIXTURE
Mix MGO Filler Dry with 7 litres of clean water per 25 kg bag.
Mix with a low speed drill (150-300 rpm) for at least three minutes to a smooth and plastic consistency. Wait for 10 minutes then mix again to ensure that the mixture is perfectly smooth and clot-free before application.
PREPARING THE DECK
Ensure that the deck is perfectly level and free from dust or other impurities.
CURING AND POT-LIFE
Use the mixture within 2 hours from mixing (at 20° C and RH 65%).
Approx. 1.2 Kg/sq.m. per mm of thickness
High-adhesion acrylic, select micro fillers, extra-pure silicon aggregates, multipurpose additives and bactericide aggregates, other additives, hydromethylcellulose.
25 Kg bags.
Store well sealed bags in an area protected from weather agents at a temperature above +5° C and below 40° C, protect from frost; do not expose to direct sunlight, life: 6 months.
|Characteristics||Value and Unit of Measure||Tolerance||Regulations|
|Chloride content||0.012%||< 0.05%||-|
|Dry extract at 105°C||99.2%||± 2%||-|
|Ash at 450°C||94,5%||± 2%||ISO/R 1515|
|Adherence to deck when dry||2.28N/mm2 (23Kg/cm2)||± 5%||ISO/R 1515|